- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 540 % | 540 % | ASTM D882 |
| Film Elongation at Break, TD | 990 % | 990 % | ASTM D882 |
| Secant Modulus, MD | 0.165 GPa | 23.9 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.170 GPa | 24.7 ksi | at 1%; ASTM D882 |
| Impact | 125 | 125 | J/mm; NOVA Chemicals Puncture test |
| Coefficient of Friction | 0.70 | 0.70 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 24.0 g/micron | 610 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | F50, ASTM D1709/A |
| Film Tensile Strength at Break, MD | 56.0 MPa | 8120 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 47.0 MPa | 6820 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | Optical properties are quoted prior to biaxial orientation; ASTM D1003 |
| Gloss | 58 % | 58 % | at 45°; Optical properties are quoted prior to biaxial orientation; ASTM D2457 |