- 密度 [g/cm3]: 0.921
- 弯曲模量 [MPa]: 0.290
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Melt Index of Compound | 0.24 g/10 min @Load 10.0 kg, Temperature 190 °C | 0.24 g/10 min @Load 22.0 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 18.1 MPa | 2630 psi | ASTM D638 |
| Elongation at Break | 340 % | 340 % | ASTM D638 |
| Flexural Modulus | 0.290 GPa | 42.1 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |