- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 750 % | 750 % | ASTM D882 |
| Elmendorf Tear Strength MD | 85 g | 85 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 250 g | 250 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.83 g/micron | 71.9 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.33 g/micron | 212 g/mil | ASTM D1922 |
| Dart drop Total Energy | 620 J/cm | 1.16 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 2.83 g/micron | 71.9 g/mil | ASTM D1709 |
| Dart drop Test | 85.0 g | 0.187 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | ASTM D882 |
| 1% Secant Modulus, MD | 300 MPa | 43500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 320 MPa | 46400 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 195 - 225 °C | 383 - 437 °F | |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | |