- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 750 % | 750 % | ASTM D882 |
| Elmendorf Tear Strength MD | 130 g | 130 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 320 g | 320 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.33 g/micron | 110 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.67 g/micron | 271.0 g/mil | ASTM D1922 |
| Dart drop Total Energy | 630 J/cm | 1.18 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 2.83 g/micron | 71.9 g/mil | ASTM D1709 |
| Dart drop Test | 85.0 g | 0.187 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
| 1% Secant Modulus, MD | 220 MPa | 31900 psi | ASTM D882 |
| 1% Secant Modulus, TD | 260 MPa | 37700 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 80 % | 80 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 185 - 205 °C | 365 - 401 °F | |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | |