- 熔体流动速率 [g/10min]: 8.5
- 密度 [g/cm3]: 0.952
- 吸水率 [%]: 0.01
- 拉伸强度 [MPa]: 26.0
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.5 g/10 min @Load 4.76 lb, Temperature 374 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| Tensile Modulus | 1.00 GPa | 145 ksi | |
| Tensile Impact Strength | 75.0 kJ/m² | 35.7 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 440 MPa | 63800 psi | |
| Tensile Creep Modulus, 1000 hours | 290 MPa | 42100 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz | 2.4 @Frequency 100 Hz | |
| 2.4 @Frequency 1e+6 Hz | 2.4 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz | 0.00020 @Frequency 100 Hz | |
| 0.00020 @Frequency 1e+6 Hz | 0.00020 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 165 µm/m-°C @Temperature 20.0 °C | 91.7 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 131 °C | 268 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
| Vicat Softening Point | 74.0 °C | 165 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm | HB @Thickness 0.0157 in | |
| Oxygen Index | 17 % | 17 % | |