- 熔体流动速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Elmendorf Tear Strength MD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 800 g | 800 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.67 g/micron | 169 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.67 g/micron | 677.4 g/mil | ASTM D1922 |
| Dart drop Total Energy | 640 J/cm | 1.20 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM D1709 |
| Dart drop Test | 120 g | 0.265 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 92 % | 92 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 265 - 300 °C | 509 - 572 °F | |
| Roll Temperature | 20.0 °C | 68.0 °F | |