- 熔体流动速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | load density; ASTM D1505 |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | 555 % | 555 % | ASTM D638 |
| Elongation at Yield | 17 % | 17 % | ASTM D638 |
| 1% Secant Modulus | 174 MPa | 25200 psi | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.80e+17 ohm-cm | 6.80e+17 ohm-cm | at 500 V; ASTM D257 |
| Dielectric Constant | 2.25 @Frequency 1000 Hz | 2.25 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | 1000 V/sec; ASTM D149 |
| Dissipation Factor | 0.00070 @Frequency 1000 Hz | 0.00070 @Frequency 1000 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 120 °C | 248 °F | Peak; SABIC Method |