Overview of materials for Very Low Density Polyethylene (VLDPE)

Overview of materials for Very Low Density Polyethylene (VLDPE) 物性表: Overview of materials for Very Low Density Polyethylene (VLDPE)物性表及特性介绍,Overview of materials for Very Low Density Polyethylene (VLDPE)注塑参数详情,如需Overview of materials for Very Low Density Polyethylene (VLDPE)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.77
  • 密度 [g/cm3]: 0.887
  • 拉伸强度 [MPa]: 4.0
  • 弯曲强度 [MPa]: 9.0
  • 弯曲模量 [MPa]: 0.0450
  • 脆化温度 [℃]: -70.0
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 0.887 - 0.923 g/cc0.0320 - 0.0333 lb/in³Average value: 0.908 g/cc Grade Count:23
Moisture Vapor Transmission 0.0300 - 0.0714 cc-mm/m²-24hr-atm0.0762 - 0.181 cc-mil/100 in²-24hr-atmAverage value: 0.0438 cc-mm/m²-24hr-atm Grade Count:3
Thickness 8.00 - 51.0 microns0.315 - 2.01 milAverage value: 29.6 microns Grade Count:16
Melt Flow 0.770 - 13.0 g/10 min0.770 - 13.0 g/10 minAverage value: 3.05 g/10 min Grade Count:23
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 26.0 - 40.026.0 - 40.0Average value: 31.3 Grade Count:3
Tensile Strength, Ultimate 9.00 - 15.0 MPa1310 - 2180 psiAverage value: 12.3 MPa Grade Count:3
Film Tensile Strength at Yield, MD 5.00 - 68.3 MPa725 - 9910 psiAverage value: 12.5 MPa Grade Count:11
Film Tensile Strength at Yield, TD 5.00 - 66.9 MPa725 - 9700 psiAverage value: 12.0 MPa Grade Count:11
Tensile Strength, Yield 4.00 - 8.00 MPa580 - 1160 psiAverage value: 5.67 MPa Grade Count:3
Film Elongation at Break, MD 400 - 800 %400 - 800 %Average value: 548 % Grade Count:12
Film Elongation at Break, TD 590 - 1000 %590 - 1000 %Average value: 790 % Grade Count:11
Elongation at Break 700 - 750 %700 - 750 %Average value: 733 % Grade Count:3
Flexural Modulus 0.0450 - 0.115 GPa6.53 - 16.7 ksiAverage value: 0.0733 GPa Grade Count:3
Secant Modulus, MD 0.0400 - 0.231 GPa5.80 - 33.5 ksiAverage value: 0.103 GPa Grade Count:8
Secant Modulus, TD 0.0500 - 0.241 GPa7.25 - 34.9 ksiAverage value: 0.113 GPa Grade Count:8
Puncture Energy 1.76 - 5.84 J1.30 - 4.31 ft-lbAverage value: 4.08 J Grade Count:3
Coefficient of Friction 0.140 - 1.000.140 - 1.00Average value: 0.498 Grade Count:9
Elmendorf Tear Strength MD 120 - 701 g120 - 701 gAverage value: 437 g Grade Count:12
Elmendorf Tear Strength TD 499 - 1030 g499 - 1030 gAverage value: 674 g Grade Count:12
Elmendorf Tear Strength, MD 3.57 - 17.7 g/micron90.6 - 450 g/milAverage value: 12.2 g/micron Grade Count:18
Elmendorf Tear Strength, TD 8.36 - 25.6 g/micron212 - 650 g/milAverage value: 19.4 g/micron Grade Count:18
Dart Drop 6.00 - 33.2 g/micron152 - 843 g/milAverage value: 22.2 g/micron Grade Count:15
Dart drop Test 120 - 210 g0.265 - 0.463 lbAverage value: 177 g Grade Count:5
Film Tensile Strength at Break, MD 13.0 - 76.6 MPa1890 - 11100 psiAverage value: 46.6 MPa Grade Count:12
Film Tensile Strength at Break, TD 20.0 - 63.6 MPa2900 - 9230 psiAverage value: 36.9 MPa Grade Count:11
 
Thermal PropertiesMetricEnglishComments
Melting Point 110 - 122 °C230 - 252 °FAverage value: 115 °C Grade Count:10
Vicat Softening Point 38.0 - 95.0 °C100 - 203 °FAverage value: 78.6 °C Grade Count:18
Brittleness Temperature -70.0 °C-94.0 °FAverage value: -70.0 °C Grade Count:7
 
Optical PropertiesMetricEnglishComments
Haze 0.600 - 25.0 %0.600 - 25.0 %Average value: 6.03 % Grade Count:15
Gloss 25.0 - 95.0 %25.0 - 95.0 %Average value: 70.8 % Grade Count:11
Transmission, Visible 90.0 %90.0 %Average value: 90.0 % Grade Count:7
 
Processing PropertiesMetricEnglishComments
Processing Temperature 86.0 - 274 °C187 - 525 °FAverage value: 188 °C Grade Count:10

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-40776.html

免责声明: 本文 Overview of materials for Very Low Density Polyethylene (VLDPE) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4