- 熔体流动速率 [g/10min]: 150.0
- 密度 [g/cm3]: 0.937
- 弯曲模量 [MPa]: 0.0360
- 脆化温度 [℃]: -40.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 18 % | 18 % | AT Plastics PTM-39 |
| Melt Flow | 150 g/10 min @Load 2.16 kg, Temperature 190 °C | 150 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 86 | 86 | ASTM D2240 |
| Hardness, Shore D | 37 | 37 | ASTM D2240 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 700 % | 700 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0360 GPa | 5.22 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 49.0 °C | 120 °F | ASTM D1525 |
| Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D746 |
| Ring & Ball Softening Point | 95.0 °C | 203 °F | ASTM E28 |