- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.917
- 弯曲模量 [MPa]: 0.190
- 脆化温度 [℃]: -25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | AT Plastics PTM-03 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 94 | 94 | ASTM D2240 |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength at Break | 7.00 MPa | 1020 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 220 % | 220 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.190 GPa | 27.6 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104.5 °C | 220.1 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Brittleness Temperature | -25.0 °C | -13.0 °F | ASTM D746 |
| Ring & Ball Softening Point | 130 °C | 266 °F | ASTM E28 |