- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 4.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 19 % | 19 % | AT Plastics PTM-39 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 190 °C | 30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | Type IV (50 mm/min); ASTM D638 |
| Tensile Strength, Yield | 4.00 MPa | 580 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 780 % | 780 % | Type IV (50 mm/min); ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | DSC; ASTM D3417 |