- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | AT Plastics PTM-03 | ||
| Thickness | >= 5.00 microns | >= 0.197 mil | Coating Thickness | ||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C | 15 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Coating Weight | 4.80 g/m² | 3.00 lb/ream | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 9.00 MPa | 1310 psi | Type IV (50 mm/min); ASTM D638 | ||
| Elongation at Break | 500 % | 500 % | Type IV (50 mm/min); ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Line Speed ft/min | < 1500 | ||||