- 熔体流动速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 12 % | 12 % | AT Plastics PTM-39 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.00 MPa | 1160 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 6.00 MPa | 870 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 410 % | 410 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 510 % | 510 % | Method A (500 mm/min); ASTM D882 |
| Dart Drop | 10.0 g/micron | 254 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 97.0 °C | 207 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 19 % | 19 % | ASTM D1003 |
| Gloss | 30 % | 30 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.1 | 2.1 | |