- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | AT Plastics PTM-03 |
| Thickness | 35.0 microns | 1.38 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 400 % | 400 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 610 % | 610 % | Method A (500 mm/min); ASTM D882 |
| Secant Modulus, MD | 0.230 GPa | 33.4 ksi | 1% Secant Modulus; ASTM D882 |
| Secant Modulus, TD | 0.270 GPa | 39.2 ksi | 1% Secant Modulus; ASTM D882 |
| Coefficient of Friction | 0.45 | 0.45 | ASTM D1894 |
| Dart Drop | 2.12 g/micron | 53.8 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 99.8 °C | 212 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 215 °C | 338 - 419 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |