- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 13.28
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | Base LE 4421; ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in³ | Catalyst LE 4472; ASTM D792 | |
| Melt Index of Compound | 0.90 g/10 min | 0.90 g/10 min | LE 4421; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 13.28 MPa | >= 1926 psi | Heat Aging (7 Days at 121°C); ASTM D412 |
| 14.8 MPa | 2140 psi | ASTM D412 | |
| Elongation at Break | >= 270 % | >= 270 % | Heat Aging (7 Days at 121°C); ASTM D412 |
| 300 % | 300 % | ASTM D412 | |
| Elongation at Yield | >= 50 % | >= 50 % | Hot Creep Test (150°C, 0.20 Mpa); ICEA T-28-562 |
| Tensile Set | <= 5.0 % | <= 5.0 % | Hot Creep Test (150°C, 0.20 Mpa); ICEA T-28-562 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.3 @Frequency 60 Hz | 2.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | >= 21.7 kV/mm | >= 550 kV/in | ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 60 Hz | 0.00050 @Frequency 60 Hz | ASTM D150 |