- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.933
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505; ASTM D1928 Proc C Mod |
| Carbon Black Loading | 2.2 % | 2.2 % | ASTM D1603 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 630 % | 630 % | Type IV (50 mm/min); ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 111 °C | 232 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Brittleness Temperature | -85.0 °C | -121 °F | ASTM D746 |