- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 8.48
- 弯曲模量 [MPa]: 0.214
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 100 hour | 100 hour | Condition B, F50; ASTM D1693 |
| Melt Index of Compound | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 8.48 MPa | 1230 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | >= 630 % | >= 630 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 0.214 GPa | 31.0 ksi | ASTM D790 |