- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 17.2
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | Base Resin; ASTM D1928/D 1505 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | Base Resin; ISO 1133 |
| Degree of Crosslinking | 12 % | 12 % | ASTM D2765 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Yield | 17.2 MPa | 2500 psi | ASTM D1238 |
| Elongation at Break | 450 % | 450 % | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.3 @Frequency 60 Hz | 2.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | >= 2.17 kV/mm | >= 55.0 kV/in | At 50 mils; ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 60 Hz | 0.00050 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |