- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 14.58
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | LE 4423; ASTM D792 | ||
| 1.05 g/cc | 0.0379 lb/in³ | LE 4432; ASTM D792 | |||
| 2.00 g/cc | 0.0723 lb/in³ | LE 4460; ASTM D792 | |||
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | LE 4423; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | >= 14.58 MPa | >= 2115 psi | Heat Aging (7 days at 121°C); ASTM D412 | ||
| 16.2 MPa | 2350 psi | ASTM D412 | |||
| Elongation at Break | <= 50 % | <= 50 % | Hot Creep Test (150°C, .2 MPa); ICEA T-28-562 | ||
| 270 % | 270 % | Heat Aging (7 days at 121°C); ASTM D412 | |||
| 300 % | 300 % | ASTM D412 | |||
| Tensile Set | <= 5.0 % | <= 5.0 % | Hot Creep Test (150°C,.2 MPa); ICE T-28-562 | ||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 2.3 @Frequency 60 Hz | 2.3 @Frequency 60 Hz | ASTM D150 | ||
| Dielectric Strength | >= 21.7 kV/mm | >= 550 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.00050 @Frequency 60 Hz | 0.00050 @Frequency 60 Hz | ASTM D150 | ||
| Processing Properties | Metric | English | Comments | ||
| Middle Barrel Temperature | >= 163 °C | >= 325 °F | |||
| Front Barrel Temperature | >= 146 °C | >= 295 °F | |||
| Die Temperature | >= 177 °C | >= 350 °F | |||
| Head Temperature | >= 177 °C | >= 351 °F | |||
| Descriptive Properties | |||||
| Horizontal Flame Test | Pass | 14AWG-30mil, UL 1581 | |||