- 熔体流动速率 [g/10min]: 0.32
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.32 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.32 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 470 % | 470 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1420 % | 1420 % | ASTM D882 | ||
| Elongation at Break | 715 % | 715 % | ASTM D638 | ||
| Coefficient of Friction | 0.73 | 0.73 | ASTM D1894 | ||
| Elmendorf Tear Strength, TD | 5.00 g/micron | 127 g/mil | ASTM D1922 | ||
| Dart Drop | 4.39 g/micron | 112 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 39.0 MPa | 5660 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 110 °C | 230 °F | Sealing Initial Temperature; Braskem® Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.0 % | 6.0 % | ASTM D1003 | ||
| Gloss | 10.8 % | 10.8 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 50 µm | ||||