- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Tensile Modulus | 0.190 GPa | 27.6 ksi | MD/TD; ASTM D882-A |
| Puncture Energy | 5.00 J | 3.69 ft-lb | 130 N; 125µm sample; ASTM D5748 |
| Coefficient of Friction | 0.60 | 0.60 | Dynamic; ISO 8295 |
| Elmendorf Tear Strength, MD | 4.077 g/micron | 103.6 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 4.89 g/micron | 124 g/mil | ISO 6383/2 |
| Dart drop Test | 450 g | 0.992 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 25.0 MPa @Temperature 24.0 °C | 3630 psi @Temperature 75.2 °F | 22mm/min; ISO 527-3 |
| Film Tensile Strength at Break, TD | 23.0 MPa @Temperature 24.0 °C | 3340 psi @Temperature 75.2 °F | 22mm/min; ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | ISO 11357-3 |
| Vicat Softening Point | 96.0 °C | 205 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 200 °C | 338 - 392 °F | |