- 熔体流动速率 [g/10min]: 7.5
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 1.0 hour @Thickness 3.00 mm, Temperature 23.0 °C | 1.0 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693 |
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 7.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | 615 % | 615 % | ASTM D638 |
| Secant Modulus | 0.149 GPa | 21.6 ksi | 0.01; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 8.5 % | 8.5 % | 60° angle; ASTM D2457 |