- 熔体流动速率 [g/10min]: 7.5
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 7.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1100 % | 1100 % | ASTM D882 | ||
| Elongation at Break | 611 % | 611 % | ASTM D638 | ||
| Coefficient of Friction | 0.86 | 0.86 | ASTM D1894 | ||
| Dart Drop | 1.97 g/micron | 50.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Sealing Initial Temperature; Braskem® Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 10.6 % | 10.6 % | ASTM D1003 | ||
| Gloss | 8.2 % | 8.2 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 10 µm | ||||