- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.915
- 拉伸强度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.915 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 1.0 hour @Thickness 3.00 mm, Temperature 23.0 °C | 1.0 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C | 30 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 484 % | 484 % | ASTM D638 |
| Secant Modulus | 0.132 GPa | 19.1 ksi | 0.01; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 8.1 % | 8.1 % | 60° angle; ASTM D2457 |