- 熔体流动速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM-D792 | ||
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 370 % | 370 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 680 % | 680 % | ASTM-D882 | ||
| Secant Modulus, MD | 0.140 GPa | 20.3 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Secant Modulus, TD | 0.150 GPa | 21.8 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 220 g | 220 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 6.00 g/micron | 152 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 4.40 g/micron | 112 g/mil | ASTM-D1922 | ||
| Dart Drop | 3.80 g/micron | 96.5 g/mil | ASTM-D1709 | ||
| Dart drop Test | 190 g | 0.419 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 13 % | 13 % | ASTM-D1003 | ||
| Gloss | 70 % | 70 % | Angle 60°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.100 cm | 0.0394 in | Blow Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 180-205 | Blow Film Extrusion | |||
| Temperature Profile (°C) | 160-205 | Blow Film Extrusion | |||