- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 80.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM-D792 | ||
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 43 | 43 | ASTM-D2240 | ||
| Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM-D638 | ||
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM-D638 | ||
| Film Elongation at Break, MD | 390 % | 390 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ASTM-D882 | ||
| Flexural Modulus, 1% Secant | 80.0 MPa | 11600 psi | Blown Film Property; ASTM-D2457 | ||
| 240 MPa | 34800 psi | Plaque Property; ASTM-D790 | |||
| Elmendorf Tear Strength TD | 55 g | 55 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 2.20 g/micron | 55.9 g/mil | ASTM-D1922 | ||
| Dart Drop | 3.60 g/micron | 91.4 g/mil | ASTM-D1709 | ||
| Dart drop Test | 90.0 g | 0.198 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 86.0 °C @Load 1.02 kg | 187 °F @Load 2.25 lb | ASTM-D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM-D1003 | ||
| Gloss | 78 % | 78 % | Angle 60°; ASTM-D2457 | ||
| Descriptive Properties | |||||
| Temperature Profile (°C) | 130-180 | Injection Molding | |||
| 180-310 | Extrusion Coating | ||||