- 密度 [g/cm3]: 0.917
- 拉伸强度 [MPa]: 9.0
- 弯曲模量 [MPa]: 0.200
- 脆化温度 [℃]: -54.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 16 g/10 min | 16 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 500 % | 500 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 85.0 °C | 185 °F | Loading 1, Rate A; ASTM D1525 |
| Brittleness Temperature | -54.0 °C | -65.2 °F | Type A, type 1 specimen; ASTM D746 |