- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 10.8
- 弯曲强度 [MPa]: 11.4
- 弯曲模量 [MPa]: 0.186
- 脆化温度 [℃]: -72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.4 MPa | 1650 psi | ASTM D638 |
| Tensile Strength, Yield | 10.8 MPa | 1570 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.186 GPa | 27.0 ksi | 3 pt. secant; ASTM D790 |
| 0.255 GPa | 37.0 ksi | 3 pt. Tangent; ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Brittleness Temperature | <= -72.0 °C | <= -97.6 °F | ASTM D746 |