- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.925
- 弯曲强度 [MPa]: 17.2
- 弯曲模量 [MPa]: 0.186
- 脆化温度 [℃]: -72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Apparent Bulk Density | 0.526 g/cc | 0.0190 lb/in³ | ASTM D1895 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.2 MPa | 2490 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 0.186 GPa | 27.0 ksi | 3 pt. secant. ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Brittleness Temperature | <= -72.0 °C | <= -97.6 °F | ASTM D746 |