- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.925
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Secant Modulus, MD | 0.160 GPa | 23.2 ksi | ASTM D882 |
| Secant Modulus, TD | 0.190 GPa | 27.6 ksi | ASTM D882 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Dart Drop | 1.30 g/micron | 33.0 g/mil | F50; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.5 % | 2.5 % | ASTM D2457 |
| Gloss | 80 % | 80 % | at 45°. ASTM D 2457 |
| 125 % | 125 % | at 60°. ASTM D 2457 | |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 204 °C | 399 °F | |