- 密度 [g/cm3]: 0.916
- 拉伸强度 [MPa]: 9.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 - 0.920 g/cc | 0.0331 - 0.0332 lb/in³ | ASTM D1505 |
| Viscosity | 57 cP @Shear Rate 3000 1/s, Temperature 190 °C | 57 cP @Shear Rate 3000 1/s, Temperature 374 °F | ASTM D3835 |
| 111 cP @Shear Rate 1000 1/s, Temperature 190 °C | 111 cP @Shear Rate 1000 1/s, Temperature 374 °F | ASTM D3835 | |
| 217000 cP @Shear Rate 300 1/s, Temperature 190 °C | 217000 cP @Shear Rate 300 1/s, Temperature 374 °F | ASTM D3835 | |
| Melt Index of Compound | 5.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 8.50 MPa | 1230 psi | ASTM D638 |
| Tensile Strength, Yield | 9.50 MPa | 1380 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 230 µm/m-°C @Temperature 20.0 °C | 128 µin/in-°F @Temperature 68.0 °F | dilatation; ASTM D696 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM D177 |
| Melting Point | 110 °C | 230 °F | ASTM D3418 |
| Vicat Softening Point | 83.0 °C | 181 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 280 °C | 374 - 536 °F | Injection Molding |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |