- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 - 0.926 g/cc | 0.0333 - 0.0335 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 0.50 - 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 - 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Elongation at Break | 575 % | 575 % | ASTM D638 |
| Secant Modulus, MD | 0.117 GPa | 17.0 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.125 GPa | 18.1 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 7.40 g/micron | 188 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.70 g/micron | 145 g/mil | ASTM D1922 |
| Dart drop Test | 160 g | 0.353 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.5 % | 8.5 % | ASTM D1003 |
| Gloss | 90 % | 90 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 155 - 165 °C | 311 - 329 °F | Plasticizing Zone; Monoextrusion |
| 165 - 175 °C | 329 - 347 °F | Mixture Zone; Monoextrusion | |
| 170 - 180 °C | 338 - 356 °F | Plasticizing Zone; Coextrusion with polyamide | |
| 180 - 190 °C | 356 - 374 °F | Mixture Zone; Coextrusion with polyamide | |
| Feed Temperature | 150 - 160 °C | 302 - 320 °F | Mono-extrusion |
| 160 - 170 °C | 320 - 338 °F | Co-extrusion with Polyamide | |
| Adapter Temperature | 175 - 185 °C | 347 - 365 °F | Mono-extrusion |
| 220 - 230 °C | 428 - 446 °F | Co-extrusion with Polyamide | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |