- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 - 0.923 g/cc | 0.0333 - 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 12.5 MPa | 1810 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 625 % | 625 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Secant Modulus, MD | 0.100 GPa | 14.5 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.110 GPa | 16.0 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.60 | 0.60 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 8.00 g/micron | 203 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.40 g/micron | 112 g/mil | ASTM D1922 |
| Dart drop Test | 180 g | 0.397 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 22.5 MPa | 3260 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.5 % | 9.5 % | ASTM D1003 |
| Gloss | 52 % | 52 % | 45° - Gardner; ASTM D2457 |
| 85 % | 85 % | @ 60° Gardner; ASTM D2457 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 155 - 165 °C | 311 - 329 °F | Plasticizing Zone |
| 165 - 175 °C | 329 - 347 °F | Mixture Zone | |
| Feed Temperature | 150 - 160 °C | 302 - 320 °F | |
| Adapter Temperature | 175 - 185 °C | 347 - 365 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |