- 密度 [g/cm3]: 0.886
- 弯曲模量 [MPa]: 0.0296
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 g/cc | 0.0320 lb/in³ | ASTM D792 |
| Melt Index of Compound | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | 1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 |
| 78 | 78 | 5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 | |
| Tensile Strength at Break | 5.93 MPa | 860 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 625 % | 625 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.0296 GPa | 4.30 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 114 °C | 237 °F | Dow Method (DSC) |
| Glass Transition Temp, Tg | -52.2 °C | -62.0 °F | reported value is for pure FLEXOMER™ DFDB-1085 NT, the primary component in this blend; Dow Method |