- 密度 [g/cm3]: 0.884
- 弯曲模量 [MPa]: 0.0310
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.884 g/cc | 0.0319 lb/in³ | ASTM D792 |
| High Load Melt Index | 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 5.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Melt Index of Compound | 0.090 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.090 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 81 | 81 | 1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 |
| 82 | 82 | 5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 | |
| Tensile Strength at Break | 8.27 MPa | 1200 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 500 % | 500 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.0310 GPa | 4.50 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 115 °C | 239 °F | Dow Method (DSC) |
| Glass Transition Temp, Tg | -47.8 °C | -54.0 °F | Dow Method |