- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 25.0 microns | 0.984 mil | ASTM D374 |
| Base Resin Melt Index | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
| Secant Modulus, MD | 0.234 GPa | 33.9 ksi | 0.01; ASTM D882 |
| Secant Modulus, TD | 0.276 GPa | 40.0 ksi | 0.01; ASTM D882 |
| Elmendorf Tear Strength, MD | 8.00 g/micron | 203 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.0 g/micron | 610 g/mil | ASTM D1922 |
| Dart Drop | 6.40 g/micron | 163 g/mil | ASTM D1709A |
| Film Tensile Strength at Break, MD | 41.0 MPa | 5950 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 102 °C | 216 °F | Eastman |
| Optical Properties | Metric | English | Comments |
| Haze | 6.5 % | 6.5 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |