- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.925
- 缺口冲击强度: 32.0
- 拉伸强度 [MPa]: 9.9
- 弯曲强度 [MPa]: 9.9
- 弯曲模量 [MPa]: 0.291
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | |
| Viscosity | 28000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 28000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 50000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 50000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 76000 cP @Shear Rate 300 1/s, Temperature 190 °C | 76000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 25 g/10 min @Load 2.16 kg | 25 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 9.1. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 9.90 MPa | 1440 psi | |
| Tensile Strength, Yield | 9.90 MPa | 1440 psi | |
| Elongation at Break | 180 % | 180 % | |
| Modulus of Elasticity | 0.186 GPa | 27.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.291 GPa | 42.2 ksi | |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² @Temperature -50.0 °C | 15.2 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | |