| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Base Resin Density | 0.915 g/cc | 0.0331 lb/in³ | ASTM D1505 | ||
| Thickness | 20.3 microns | 0.799 mil | ASTM D374 | ||
| Base Resin Melt Index | 0.55 g/10 min | 0.55 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, TD | 9.70 MPa | 1410 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 | ||
| Film Elongation at Break, TD | 930 % | 930 % | ASTM D882 | ||
| Secant Modulus, MD | 0.187 GPa | 27.1 ksi | 0.01; ASTM D882 | ||
| Secant Modulus, TD | 0.244 GPa | 35.4 ksi | 0.01; ASTM D882 | ||
| Elmendorf Tear Strength, MD | 18.22 g/micron | 462.8 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 45.81 g/micron | 1164 g/mil | ASTM D1922 | ||
| Dart Drop | 7.88 g/micron | 200 g/mil | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 39.0 MPa | 5660 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.3 % | 3.3 % | ASTM D1003 | ||
| Gloss | 83 % | 83 % | at 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Peel Cling, Aged 2 Weeks, 0% | 360 g | ||||
| Peel Cling, Aged 2 Weeks, 200% | 260 g | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.