- 透光率 [%]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Base Resin Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D4883 | ||
| Water Vapor Transmission | 18.6 g/m²/day | 1.20 g/100 in²/day | ASTM F372 | ||
| Oxygen Transmission | 200 cc-mm/m²-24hr-atm | 508 cc-mil/100 in²-24hr-atm | ASTM D3985 | ||
| Thickness | 31.75 microns | 1.250 mil | |||
| Base Resin Melt Index | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 24.0 MPa | 3480 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Secant Modulus, MD | 0.172 GPa | 24.9 ksi | 0.01; ASTM D882 | ||
| Secant Modulus, TD | 0.193 GPa | 28.0 ksi | 0.01; ASTM D882 | ||
| Coefficient of Friction | 0.25 | 0.25 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.08 g/micron | 256.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 5.35 g/micron | 136 g/mil | ASTM D1922 | ||
| Dart Drop | 2.36 g/micron | 59.9 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.5 % | 4.5 % | ASTM D1003 | ||
| Gloss | 75 % | 75 % | at 45°; ASTM D2457 | ||
| Transmission, Visible | 50 % | 50 % | Transparency; ASTM D1746 | ||
| Descriptive Properties | |||||
| Process | Film | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.