- 熔体流动速率 [g/10min]: 3.5
- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.130
- 脆化温度 [℃]: -75.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.920 g/cc | 0.920 g/cc | ISO 1183 |
Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 47 | 47 | ISO 868/A |
Tensile Strength, Yield | 11.0 MPa | 1600 psi | ISO 527 |
Flexural Modulus | 0.130 GPa | 18.9 ksi | ISO 178 |
Thermal Properties | Metric | English | Comments |
Melting Point | 110 °C | 230 °F | Internal method |
Vicat Softening Point | 90.0 °C @Load 1.00 kg | 194 °F @Load 2.20 lb | ISO 306/A |
Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |