Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.918 g/cc | 0.918 g/cc | ISO 1183 |
Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 45 | 45 | ISO 868/A |
Tensile Strength, Yield | 10.0 MPa | 1450 psi | ISO 527 |
Flexural Modulus | 0.120 GPa | 17.4 ksi | ISO 178 |
Thermal Properties | Metric | English | Comments |
Melting Point | 107 °C | 225 °F | Internal method |
Vicat Softening Point | 84.0 °C @Load 1.00 kg | 183 °F @Load 2.20 lb | ISO 306/A |
Brittleness Temperature | <= -20.0 °C | <= -4.00 °F | ASTM D746 |