- 熔体流动速率 [g/10min]: 3.0
- 脆化温度 [℃]: -70.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ISO 1183 |
| Thickness | 8.00 - 50.0 microns | 0.315 - 1.97 mil | Recommended |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 5.00 MPa | 725 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 5.00 MPa | 725 psi | ISO 527-3 |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 527-3 |
| Film Elongation at Break, TD | 800 % | 800 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 4.076 g/micron | 103.5 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 8.3558 g/micron | 212.24 g/mil | ISO 6383-2 |
| Dart drop Test | 210 g | 0.463 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 50.0 MPa | 7250 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 115 °C | 239 °F | Internal method |
| Vicat Softening Point | 54.0 °C @Load 1.00 kg | 129 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ISO 14782 |
| Gloss | 84 % | 84 % | 45°; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |