- 熔体流动速率 [g/10min]: 50.0
- 拉伸强度 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ASTM D792 |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 8.96 MPa | 1300 psi | ASTM D638 |
| Tensile Strength, Yield | 11.7 MPa | 1700 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| 2% Secant Modulus | 0.345 GPa | 50.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 97.8 °C | 208 °F | Rate A (50°C/h), Loading 1 (10 N); ASTM D1525 |