- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 11.9 MPa | 1720 psi | Data derived from Type IV specimen, 75 mil plaques, @ 20" min.; ASTM D638 | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elongation at Break | 650 % | 650 % | Molded; ASTM D638 | ||
| Elmendorf Tear Strength MD | 380 g | 380 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 | ||
| Dart drop Test | 90.0 g | 0.198 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 23.4 MPa | 3400 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.2 MPa | 2500 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 193 MPa | 28000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 221 MPa | 32000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.0 % | 6.0 % | ASTM D1003 | ||
| Gloss | 70 % | 70 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Antiblock | Medium | ||||
| Slip | Medium | ||||