- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 14.5
- 弯曲模量 [MPa]: 0.234
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Environmental Stress Crack Resistance | >= 168 hour | >= 168 hour | Cond. A 100% lgepal, 0 failures in 7 days; ASTM D1693 | ||
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 | 50 | Molded; ASTM D2240 | ||
| Tensile Strength, Yield | 14.5 MPa | 2100 psi | Molded; ASTM D638 | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elongation at Break | >= 600 % | >= 600 % | Molded; ASTM D638 | ||
| Flexural Modulus | 0.234 GPa | 34.0 ksi | Molded; ASTM D790 | ||
| Elmendorf Tear Strength MD | 220 g | 220 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 | ||
| Dart drop Test | 220 g | 0.485 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 20.7 MPa | 3000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 19.3 MPa | 2800 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 165 MPa | 24000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 186 MPa | 27000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | Molded; F50; ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | |||
| Descriptive Properties | |||||
| Antiblock | None | ||||
| Slip | None | ||||