- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 10.7
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 46 | 46 | Molded; ASTM D2240 |
| Tensile Strength at Break | 11.4 MPa | 1650 psi | Molded; ASTM D638 |
| Tensile Strength, Yield | 10.7 MPa | 1550 psi | Molded; ASTM D638 |
| Film Elongation at Break, MD | 160 % | 160 % | ASTM D882 |
| Film Elongation at Break, TD | 480 % | 480 % | ASTM D882 |
| Elongation at Break | 700 % | 700 % | Molded; ASTM D638 |
| Elongation at Yield | 100 % | 100 % | Molded; ASTM D638 |
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 180 g | 180 g | ASTM D1922 |
| Dart drop Test | 130 g | 0.287 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.4 MPa | 3400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.5 MPa | 2400 psi | ASTM D882 |
| 1% Secant Modulus, MD | 179 MPa | 26000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 221 MPa | 32000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Brittleness Temperature | -75.0 °C | -103 °F | Molded; F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 177 °C | 350 °F | |