- 熔体流动速率 [g/10min]: 9.0
- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 8.96
- 弯曲模量 [MPa]: 0.255
- 热变形温度 [℃]: 40.0
- 脆化温度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ASTM D2240 |
| Tensile Strength, Yield | 8.96 MPa | 1300 psi | ASTM D638 |
| Elongation at Yield | 14 % | 14 % | ASTM D638 |
| Flexural Modulus | 0.255 GPa | 37.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |
| Brittleness Temperature | -65.0 °C | -85.0 °F | F50; ASTM D746 |