- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 6000 ppm | 6000 ppm | |||
| Slip Level | 1600 ppm | 1600 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.00 MPa | 1160 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.38 MPa | 1070 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 | ||
| Film Elongation at Break, TD | 540 % | 540 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.1 % | 7.1 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.8 % | 5.8 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 180 g | 180 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 7.346 g/micron | 186.6 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 | ||
| Dart Drop | 1.83 g/micron | 46.6 g/mil | ASTM D1709 | ||
| Dart drop Test | 70.0 g | 0.154 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.9 MPa | 3320 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 13.5 MPa | 1960 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 152 MPa | 22000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 163 MPa | 23600 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 109 °C | 228 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 96.0 °C | 205 °F | ExxonMobil Method | ||
| Vicat Softening Point | 93.3 °C | 200 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM D1003 | ||
| Gloss | 72 % | 72 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.