- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.929
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 1000 ppm | 1000 ppm | |||
| Slip Level | 250 ppm | 250 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 13.8 MPa | 2000 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 15.9 MPa | 2300 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 160 % | 160 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Puncture Energy | 0.339 J | 0.250 ft-lb | ExxonMobil Method | ||
| Elmendorf Tear Strength MD | 180 g | 180 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 240 g | 240 g | ASTM D1922 | ||
| Dart drop Test | 80.0 g | 0.176 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.8 MPa | 3600 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 317 MPa | 46000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 379 MPa | 55000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 116 °C | 241 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.2 % | 7.2 % | ASTM D1003 | ||
| Gloss | 68 % | 68 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||