- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 250 g | 250 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 7.87 g/micron | 200 g/mil | ASTM D1922 |
| Dart Drop | 2.36 g/micron | 60.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 75.0 g | 0.165 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 109 °C | 228 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 40 % | 40 % | 45°, ASTM D-2457 |